The effects of porosity on in vitro degradation of polylactic acid- polyglycolic acid implants used in repair of articular cartilage

K. A. Athanasiou, J. P. Schmitz, C. M. Agrawal

Research output: Contribution to journalArticle

87 Citations (Scopus)

Abstract

The objective of this study was to examine the effects of porosity on in vitro degradation characteristics of an osteochondral biodegradable implant made of a 50:50 copolymer of polylactic acid-polyglycolic acid. Ninety specimens were produced to represent three porosities: approximately 0% (low porosity), 33% (medium porosity), and 75% (high porosity). These specimens were allowed to degrade in phosphate-buffered saline at 37°C for 8 weeks or until essentially complete degradation was achieved. Degradation of the specimens was examined using creep indentation mechanical testing, pH measurements, mass loss quantification, molecular weight loss measurements, gross morphology, and scanning electron microscopy. The results indicate that specimen porosity has important implications insofar as implant structural properties are concerned. In general, low-porosity implants underwent significantly larger losses in molecular weight than medium- or high-porosity specimens. Although no significant decreases in mass loss were found for any group for up to 4 weeks, between 4 and 6 weeks a significant drop in mass was observed in all groups. This drop was most severe in the low-porosity group. Mechanical testing showed that high- and low-porosity specimens were two to three times stiffer (Young's modulus and shear modulus) than medium-porosity specimens at 0 weeks. Measurement of pH demonstrated that with decreasing porosity, the implant pH values became significantly more acidic. It thus appears that low-porosity specimens undergo faster degradation than either medium- or high-porosity specimens. As a result, low porosity may contribute to shortening of the functional life of the implant. This may be due to enhanced autocatalysis in those implants, which are unable to evacuate acidic degradation by-products.

Original languageEnglish (US)
Pages (from-to)53-63
Number of pages11
JournalTissue Engineering
Volume4
Issue number1
DOIs
StatePublished - 1998
Externally publishedYes

Fingerprint

Polyglycolic Acid
Porosity
Cartilage
Articular Cartilage
Repair
Degradation
Acids
poly(lactic acid)
In Vitro Techniques
Mechanical testing
Absorbable Implants
Molecular Weight
Elastic moduli
Molecular weight
Elastic Modulus

ASJC Scopus subject areas

  • Biophysics
  • Cell Biology

Cite this

The effects of porosity on in vitro degradation of polylactic acid- polyglycolic acid implants used in repair of articular cartilage. / Athanasiou, K. A.; Schmitz, J. P.; Agrawal, C. M.

In: Tissue Engineering, Vol. 4, No. 1, 1998, p. 53-63.

Research output: Contribution to journalArticle

@article{383c08f2fc8e49fa9263f9688cf102ac,
title = "The effects of porosity on in vitro degradation of polylactic acid- polyglycolic acid implants used in repair of articular cartilage",
abstract = "The objective of this study was to examine the effects of porosity on in vitro degradation characteristics of an osteochondral biodegradable implant made of a 50:50 copolymer of polylactic acid-polyglycolic acid. Ninety specimens were produced to represent three porosities: approximately 0{\%} (low porosity), 33{\%} (medium porosity), and 75{\%} (high porosity). These specimens were allowed to degrade in phosphate-buffered saline at 37°C for 8 weeks or until essentially complete degradation was achieved. Degradation of the specimens was examined using creep indentation mechanical testing, pH measurements, mass loss quantification, molecular weight loss measurements, gross morphology, and scanning electron microscopy. The results indicate that specimen porosity has important implications insofar as implant structural properties are concerned. In general, low-porosity implants underwent significantly larger losses in molecular weight than medium- or high-porosity specimens. Although no significant decreases in mass loss were found for any group for up to 4 weeks, between 4 and 6 weeks a significant drop in mass was observed in all groups. This drop was most severe in the low-porosity group. Mechanical testing showed that high- and low-porosity specimens were two to three times stiffer (Young's modulus and shear modulus) than medium-porosity specimens at 0 weeks. Measurement of pH demonstrated that with decreasing porosity, the implant pH values became significantly more acidic. It thus appears that low-porosity specimens undergo faster degradation than either medium- or high-porosity specimens. As a result, low porosity may contribute to shortening of the functional life of the implant. This may be due to enhanced autocatalysis in those implants, which are unable to evacuate acidic degradation by-products.",
author = "Athanasiou, {K. A.} and Schmitz, {J. P.} and Agrawal, {C. M.}",
year = "1998",
doi = "10.1089/ten.1998.4.53",
language = "English (US)",
volume = "4",
pages = "53--63",
journal = "Tissue Engineering",
issn = "1076-3279",
publisher = "Mary Ann Liebert Inc.",
number = "1",

}

TY - JOUR

T1 - The effects of porosity on in vitro degradation of polylactic acid- polyglycolic acid implants used in repair of articular cartilage

AU - Athanasiou, K. A.

AU - Schmitz, J. P.

AU - Agrawal, C. M.

PY - 1998

Y1 - 1998

N2 - The objective of this study was to examine the effects of porosity on in vitro degradation characteristics of an osteochondral biodegradable implant made of a 50:50 copolymer of polylactic acid-polyglycolic acid. Ninety specimens were produced to represent three porosities: approximately 0% (low porosity), 33% (medium porosity), and 75% (high porosity). These specimens were allowed to degrade in phosphate-buffered saline at 37°C for 8 weeks or until essentially complete degradation was achieved. Degradation of the specimens was examined using creep indentation mechanical testing, pH measurements, mass loss quantification, molecular weight loss measurements, gross morphology, and scanning electron microscopy. The results indicate that specimen porosity has important implications insofar as implant structural properties are concerned. In general, low-porosity implants underwent significantly larger losses in molecular weight than medium- or high-porosity specimens. Although no significant decreases in mass loss were found for any group for up to 4 weeks, between 4 and 6 weeks a significant drop in mass was observed in all groups. This drop was most severe in the low-porosity group. Mechanical testing showed that high- and low-porosity specimens were two to three times stiffer (Young's modulus and shear modulus) than medium-porosity specimens at 0 weeks. Measurement of pH demonstrated that with decreasing porosity, the implant pH values became significantly more acidic. It thus appears that low-porosity specimens undergo faster degradation than either medium- or high-porosity specimens. As a result, low porosity may contribute to shortening of the functional life of the implant. This may be due to enhanced autocatalysis in those implants, which are unable to evacuate acidic degradation by-products.

AB - The objective of this study was to examine the effects of porosity on in vitro degradation characteristics of an osteochondral biodegradable implant made of a 50:50 copolymer of polylactic acid-polyglycolic acid. Ninety specimens were produced to represent three porosities: approximately 0% (low porosity), 33% (medium porosity), and 75% (high porosity). These specimens were allowed to degrade in phosphate-buffered saline at 37°C for 8 weeks or until essentially complete degradation was achieved. Degradation of the specimens was examined using creep indentation mechanical testing, pH measurements, mass loss quantification, molecular weight loss measurements, gross morphology, and scanning electron microscopy. The results indicate that specimen porosity has important implications insofar as implant structural properties are concerned. In general, low-porosity implants underwent significantly larger losses in molecular weight than medium- or high-porosity specimens. Although no significant decreases in mass loss were found for any group for up to 4 weeks, between 4 and 6 weeks a significant drop in mass was observed in all groups. This drop was most severe in the low-porosity group. Mechanical testing showed that high- and low-porosity specimens were two to three times stiffer (Young's modulus and shear modulus) than medium-porosity specimens at 0 weeks. Measurement of pH demonstrated that with decreasing porosity, the implant pH values became significantly more acidic. It thus appears that low-porosity specimens undergo faster degradation than either medium- or high-porosity specimens. As a result, low porosity may contribute to shortening of the functional life of the implant. This may be due to enhanced autocatalysis in those implants, which are unable to evacuate acidic degradation by-products.

UR - http://www.scopus.com/inward/record.url?scp=0031893301&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0031893301&partnerID=8YFLogxK

U2 - 10.1089/ten.1998.4.53

DO - 10.1089/ten.1998.4.53

M3 - Article

AN - SCOPUS:0031893301

VL - 4

SP - 53

EP - 63

JO - Tissue Engineering

JF - Tissue Engineering

SN - 1076-3279

IS - 1

ER -