Glass-like lattice thermal conductivity and high thermoelectric efficiency in Yb9Mn4.2Sb9

Sabah K. Bux, Alexandra Zevalkink, Oliver Janka, David Uhl, Susan Kauzlarich, Jeffrey G. Snyder, Jean Pierre Fleurial

Research output: Contribution to journalArticlepeer-review

81 Scopus citations

Abstract

Motivated by excellent thermoelectric performance in the well-known Yb-based Zintl compounds Yb14MnSb11 and YbZn 2-xMnxSb2, this study investigates the thermoelectric properties of Yb9Mn4.2Sb9. Unlike most transition metal containing Zintl phases, Yb9Mn 4.2Sb9 contains a partially occupied Mn site and thus does not have a valence-precise stoichiometry. Samples were synthesized by direct ball milling of the elements, followed by hot pressing. Consistent with previous reports, X-ray diffraction and wavelength dispersive spectroscopy confirmed a narrow composition range near Yb9Mn4.2Sb9. High temperature measurements of the electronic properties of Yb9Mn 4.2Sb9 indicate that it is a degenerate p-type semiconductor with a band gap sufficiently large for high temperature thermoelectric applications. Hall measurements reveal that Yb9Mn 4.2Sb9 has a high extrinsic carrier concentration (∼1020 h+ cm-3), which is due to the deviation from the theoretical "Zintl composition" of Yb 9Mn4.5Sb9. The measured carrier concentration coincides with the optimum concentration predicted using a single parabolic band model. Measurements of the thermal diffusivity and heat capacity reveal an extremely low, temperature-independent lattice thermal conductivity in this compound (κL < 0.4 W mK-1), which is due to both the large unit cell size (44 atoms per primitive cell) and substantial disorder on the Mn site. This favorable combination of optimized electronic properties and low lattice thermal conductivity leads to a promising figure of merit at high temperature (zT = 0.7 at 950 K).

Original languageEnglish (US)
Pages (from-to)215-220
Number of pages6
JournalJournal of Materials Chemistry A
Volume2
Issue number1
DOIs
StatePublished - Jan 7 2014

ASJC Scopus subject areas

  • Chemistry(all)
  • Renewable Energy, Sustainability and the Environment
  • Materials Science(all)

Fingerprint Dive into the research topics of 'Glass-like lattice thermal conductivity and high thermoelectric efficiency in Yb<sub>9</sub>Mn<sub>4.2</sub>Sb<sub>9</sub>'. Together they form a unique fingerprint.

Cite this